2005 Ford Cvpi recalls and problems

In its recall notice dated August 26, 2013, Ford Motor Company (Ford) notified NHTSA of a safety defect condition that may result in loss of steering in approximately 355,000 model year (MY) 2005 through 2011 Ford Crown Victoria and Mercury Grand Marquis vehicles built at the St. Thomas Assembly Plant, MY 2005 through 2007 Lincoln Town Car vehicles built at the Wixom Assembly Plant, and certain MY 2008 through 2011 Lincoln Town Car vehicles built at the St. Thomas Assembly Plant and that are currently registered or were originally sold in Connecticut, Delaware, the District of Columbia, Illinois, Indiana, Iowa, Kentucky, Maine, Maryland, Massachusetts, Michigan, Minnesota, Missouri, New Hampshire, New Jersey, New York, Ohio, Pennsylvania, Rhode Island, Vermont, Virginia, West Virginia, or Wisconsin (NHTSA Recall 13V-385, Ford Recall 13S08).Ford's recall addresses a corrosion related defect in the lower intermediate shaft that may result in separation of the steering column lower bearing and loss of steering control.Ford's recall will remedy the defect condition by instructing dealers to replace the lower intermediate shaft and to inspect and repair the upper intermediate shaft and steering column lower bearing as necessary.A retaining clip will be installed if the lower bearing has separated.Ford's investigation of steering column separations in the subject vehicles identified a defect condition in the lower intermediate shaft that could result in separation of the column low…

FRACTURE (CRACKING) OF THE SUBJECT VEHICLE (SV) WHEEL, WHICH WAS PREVIOUSLY INVESTIGATED UNDER PRELIMINARY EVALUATION PE03-009 (SAFETY RECALL 03V-279), OCCURS IN THE MODEL YEAR (MY) 2003 TO 2005 POLICE INTERCEPTOR VEHICLES ONLY; CIVILIAN SPECIFICATION AND OTHER MY VEHICLES ARE UNAFFECTED BY THIS CONDITION.FOR THE AFFECTED SUBJECT WHEELS, A FATIGUE CRACK OCCURS IN THE HEAT AFFECTED ZONE OF THE RIM MATERIAL ADJACENT TO THE CIRCUMFERENTIAL WELD THAT ATTACHES THE RIM TO THE OUTBOARD WHEEL DISC.THE CRACK INITIATES UNDER THE OUTBOARD TIRE BEAD NEAR THE HEEL (WHERE AIR LEAKAGE CANNOT BE ASSURED) AND SUBSEQUENTLY GROWS CIRCUMFERENTIALLY THROUGH CYCLIC BENDING AS THE WHEELS ROLLS.ALTHOUGH THE VAST MAJORITY OF RIM CRACKS EITHER PRESENTED NO SYMPTOMS OR WERE DETECTED SAFELY VIA RECURRING SLOW AIR LEAKAGE, ODI IDENTIFIED 6 INCIDENTS WHERE RAPID AIR LEAKAGE LEADING TO A FULL OR PARTIAL DEFLATION OF THE TIRE WAS ALLEGED.FOR THESE WHEELS, EVIDENCE INDICATED THAT MULTIPLE CRACKS HAD FORMED IN DIFFERENT AREAS OF THE RIM AND SUBSEQUENTLY GROWN TOGETHER.TWO OF THE INCIDENTS RESULTED IN A CRASH, ONE DURING A HIGH SPEED PURSUIT.ALTHOUGH THE MINORITY OF CASES, FORD?S ASSESSMENTS OF FIELD RETURN WHEELS SHOWED THAT MULTIPLE CRACKS EXIST IN APPROXIMATELY 17 PERCENT OF THE CRACKED WHEELS REPLACED UNDER A FORD EXTENDED WARRANTY PROGRAM.IN A WHEEL WITH MULTIPLE CRACKS, AS THE AREA BETWEEN THE CRACKS IS REDUCED BY GROWTH A HIGH STRESS CONDITION (SUCH AS WOULD OCCUR IN AN AGGRESSIVE VEHICLE MANEUVER DURIN…

DURING A SEPTEMBER 23, 2004 MEETING AND IN SUBSEQUENT DISCUSSIONS IN NOVEMBER, FORD ADVISED THE OFFICE OF DEFECTS INVESTIGATION (ODI) OF THEIR PLANS TO INTRODUCE AN IMPROVED STEEL WHEEL FOR MANUFACTURING AND SERVICE COMPONENT USE ON THE SUBJECT VEHICLES, INDICATING THIS WOULD OCCUR IN DECEMBER 2004.THE NEW WHEEL DESIGN INCORPORATES AN ADDITIONAL MANUFACTURING PROCESS (SHOT PEENING) WHICH LOWERS TENSILE STRESS IN THE SURFACE LAYER OF THE RIM MATERIAL ADJACENT TO THE CIRCUMFERENTIAL WELD. THEORETICALLY THIS SHOULD IMPROVE RIM DURABILITY BY REDUCING FATIGUE CRACK INITIATION SITES.INDICATIONS FROM FORD?S ACCELERATED TESTING METHODS SHOW AN IMPROVEMENT IN THE PERFORMANCE OF THE NEW WHEEL.IN ADDITION TO PRIOR SAFETY RECALL 03V279 AND SERVICE ACTION (SA) 03M03, FORD WILL ANNOUNCE A NEW EXTENDED WARRANTY SA FOR VEHICLES BUILT PRIOR TO DECEMBER 2004 THAT SUFFER RIM FRACTURES IN SERVICE.THE NEW WHEEL DESIGN WILL BE USED AS A REMEDY.FORD ADVISES THAT A SA IS SUFFICIENT FOR ADDRESSING FUTURE WHEEL FAILURES (INCLUDING RECALL 03V279 REMEDY WHEEL FAILURES) BECAUSE: 1) FAILURE RATES ARE LOW BASED ON FORD?S ANALYSIS, AND 2) DRIVER WARNINGS (REPETITIVE SLOW AIR LOSS, AND OR STEERING WHEEL VIBRATION) ALLOW EARLY AND SAFE DETECTION OF CRACKED WHEELS.ODI HAS RECEIVED 25 VEHICLE OWNER QUESTIONNAIRE (VOQ) REPORTS (INVOLVING 22 VEHICLES) WHICH ALLEGE A RIM FRACTURE OF ONE OR MORE STEEL WHEELS.ABOUT HALF THE REPORTS INVOLVE VEHICLES BUILT WITH THE REMEDY WHEEL USED FOR RECALL 03V279, AND MOST OF THE …